The “13th Five-Year” plastics industry will accelerate the development of the industry chain in the blank sector

[Jiuzhi Plastics News] At the 2016 Petrochemical Industry Development Conference held on April 12, the China Petroleum and Chemical Industry Federation issued the "13th Five-Year" Development Guide for Petroleum and Chemical Industry (referred to as the "Guide"). During the “Thirteenth Five-Year Plan” period, the annual growth rate of the industry will be transformed into single digits, and the structure will make significant progress. The proportion of strategic emerging industries such as new chemical materials will increase significantly.
In the petrochemical industry, we will strive to achieve breakthroughs in optimizing industrial layout and raw material structure, and promoting high-end products. At the same time, we will strictly limit the growth of new refining capacity and strive to stabilize domestic refining capacity at around 850 million tons in 2020.
In the field of new chemical materials, accelerate the industrialization of blank products. Advance the research and development of engineering plastics such as PC (polycarbonate) and PEEN (polyether ether nitrile), high-end polyolefin resins such as metallocene polyethylene and metallocene polypropylene, and phenyl silicone monomers, and actively develop halogenated butyl and hydrogenated Rubber with special properties such as nitrile and new thermoplastic elastomer. Reduce costs, improve product quality, focus on breaking through the low-cost, stable and large-scale production technology of domestic T300 and T700 carbon fiber, and improve the quality of POM, PET/PBT resin, polyphenylene sulfide, nylon and other engineering plastics. . Break through the supply bottleneck of key upstream supporting raw materials, accelerate the development of key supporting monomers such as adiponitrile and CHDM (1,4-cyclohexane dimethanol) and engineering plastic alloys, and accelerate the high carbon of hexene-1 and octene-1. Research and development of α-olefin comonomers to promote the industrialization of high-performance polyolefins.
In addition, the promotion of new chemical materials in new application areas is expected to accelerate, including the promotion of environmentally friendly polyurethanes in the field of building energy conservation; the development of high-end fluorine, silicon polymers, fluorine-containing functional membrane materials and chemicals; The application of the industry; at the same time accelerate the development of new energy batteries, integrated circuits and other fields supporting electronic chemicals.
For the modern coal chemical industry, it will adhere to rational layout, water quantity, clean and efficient conversion, and carry out the demonstration of key technologies and industrialization upgrades of modern coal chemical industry. In the field of bio-chemicals, improve the technical level and economy, promote the large-scale commercial application of bio-based new materials, bio-based chemicals and bio-fuels; accelerate the development of bio-medical materials to meet the rapidly growing market demand.

Hdpe Anti-Root Membrane Use high strength polyethylene after extrusion, smooth surface with high corrosion and weather resistance, waterproof effect is good, thorn resistance significantly. Suitable for planting roof, Roof garden, the garage roof greening and need the underground building roof engineering.

1) Has excellent waterproof function, can form high strength waterproof layer, the ability to resist water pressure is strong, maintain the long-term effects of water;
  2) Has prevented the plant root penetration function, can withstand the plant root system puncture. Preventing root, but also does not affect the normal growth of plants;
  3) The product of high tensile strength, corrosion resistance, mold resistance, good weatherability;

  4) Excellent high and low temperature performance of base contraction deformation and cracking of the strong ability to adapt, suitable for hot and cold region can be.


  5) Hot melt method construction, convenient construction and hot joint reliability and durability, the four seasons can operation.

HDPE Anti-root membrane

                       Spec

Properties

GM1.0

GM1.25

GM1.5

GM2.0

GM2.5

Thickness

1.00mm

1.25mm

1.50mm

2.00mm

2.50mm

Density ( ≥)

0.940g/cc

0.940g/cc

0.940g/cc

0.940g/cc

0.940g/cc

Tensile Properties ( ≥)

•   yield strength

•   break strength

•   yield elongation

•   break elongation

 

13 kN/m

20 kN/m

11%

600%

 

16 kN/m

25 kN/m

11%

600%

 

20 kN/m

30 kN/m

11%

600%

 

26 kN/m

40 kN/m

11%

600%

 

33kN/m

50kN/m

11%

600%

Tear Resistance ( ≥)

115 N

140 N

170 N

225 N

280 N

Puncture Resistance ( ≥)

240 N

300 N

360 N

480 N

600 N

Carbon Black Content ( ≥)

2.0-3.0%

2.0-3.0%

2.0-3.0%

2.0-3.0%

2.0-3.0%

Carbon Black Dispersion ( ≥)

Note(1)

Note(1)

Note(1)

Note(1)

Note(1)

Oxidative Induction Time(OIT)

Standard OIT ( ≥)

 

60 min.

 

60 min.

 

60 min.

 

60 min.

 

60 min

HDPE Anti-root Membrane

Hdpe Anti-Root Membrane,Hdpe Dimple Membrane,Plastic Sheet Membrane,Waterproofing Membrane

Shandong Tianhai New Materials Engineering Co., Ltd , https://www.chinatinhy.com