How to carry out alkaline etching of aluminum castings?

[China Aluminum Industry Network] In addition to containing free silicon, aluminum parts also contain various compounds and other inclusions between metals. Due to the loose structure of the cast aluminum parts, there may be uneven segregation of chemical components. At the same time, the unprocessed surface will form a dense oxide film when cooled after casting. Alkali corrosion time is short, the cast aluminum may not be completely removed, and due to alkaline dissolution of cast aluminum when the dissolution rate is faster, after alkali etching will often lead to excessive corrosion of cast aluminum parts, resulting in tolerance size Changes can even cause product obsolescence.

In view of the existence of the above situation, it can be solved by changing the alkali etching procedure, that is, the alkali etching treatment is performed after the casting molding. According to this process procedure, it is possible to prevent problems such as scrapping of parts caused by alkali corrosion, and also to facilitate the surface quality after oxidation.

The above-mentioned alkali etching method can avoid over-corrosion of the parts, and after alkali etching, 1:1 hydrochloric acid can be used for rapid light emission of 2 to 3 seconds instead of the more toxic hydrofluoric acid, which is not only favorable for environmental protection, but also improves working conditions. It can also reduce production costs.

Tip Combs

These tip combs are for use with the Pharma KingFisher Flex 96 Deep-Well Head Magnetic Particle Processor or MagMAX Express-96 Deep-Well Magnetic Particle Processor in combination with PrepSEQ ResDNA kits and ProteinSEQ kits.
Optimize performance using KingFisher Flex System consumables designed specifically for use with these instruments. KingFisher Flex disposable plastics (tip combs and microplates) are made of polypropylene and are ideal for magnetic particle processing because of their low binding affinity for biomolecules. Their special design enables excellent recovery of magnetic beads.
The tip combs are made of PP material, they can be used with 2.2ml square well V bottom and 0.5ml elution plates for the system KINGFISHER FLEX. The tip combs could suffer centrifuge 3000-4000 and don't change the original shape. The products are suitable for the standard ANSI and multi-channel Pipette Tips machnie and automatic equipment. We could accept OEM/ODM.

For use with Viral RNA extraction, DNA extraction, RNA/DNA quantification, immunopreciptitations and many more KingFisherâ„¢ applications
good chemical and physical resistance: e.g. phenols, chloroform, DMSO and temperatures as low as -80°C/-112°F

Tip Comb,Tip Comb Plate,Kingfisher Tip Comb,Tip Comb Kingfisher,Magnetic Tip Comb,8-Strip Tip Comb

Yong Yue Medical Technology(Kunshan) Co.,Ltd , https://www.yonyuemedicals.com